HEMPADUR 海虹油漆15590老人牌15599

HEMPADUR 1559015590: BASE 15599: CURING AGENT 95100

Description: Recommended use: Service temperature: Certificates/Approvals: Availability: HEMPADUR 15590 is a two-component epoxy primer coating especially for use on surfaces exposed  to severe abrasion. As a blast primer for heavy duty epoxy systems on submerged and non-submerged areas according to  specification. For use at temperatures of 5°C/41°F, preferably 10°C/50°F or higher. Maximum, dry exposure only: 140°C/284°F Part of Group Assortment. Local availability subject to confirmation. HEMPADUR 15590 15590: BASE 15599: CURING AGENT 95100 Product Data PHYSICAL CONSTANTS: The physical constants stated are nominal data according to the HEMPEL Group&＃39;s approved formulas. Shade nos/Colours: Finish: Volume solids, %: Theoretical spreading rate: VOC content: Fully cured: Dry to touch: Specific gravity: Flash point: - 56880 / Red. Semi-gloss 44 ± 1 11 m2 /l [441.1 sq.ft./US gallon] - 40 micron/1.6 mils 3 approx. hour(s) 20°C/68°F 7 day(s) 20°C/68°F 26 °C [78.8 °F] 1.3 kg/litre [11 lbs/US gallon] 498 g/l [4.1 lbs/US gallon] Shelf life: 1 year for BASE and 3 years for CURING AGENT (stored in closed container) (25°C/77°F) from time  of production. Depending on storage conditions, mechanical stirring may be necessary before usage. APPLICATION DETAILS: Version, mixed product: Mixing ratio: Application method: Thinner (max.vol.): 15590 15 : 4 by volume Airless spray / Air spray 08450 (5%) / 08450 (15%) Pot life: Nozzle orifice: 2 hour(s) 20°C/68°F 0.017 - 0.019 " Nozzle pressure: 150 bar [2175 psi] (Airless spray data are indicative and subject to adjustment) Indicated film thickness, dry: 40 micron [1.6 mils] Indicated film thickness, wet: 100 micron [4 mils] Overcoat interval, min: see REMARKS overleaf Overcoat interval, max: see REMARKS overleaf BASE 15599: CURING AGENT 95100 Safety: Handle with care. Before and during use, observe all safety labels on packaging and paint containers, consult HEMPEL Safety Data Sheets and follow all local or national safety regulations. Cleaning of tools: HEMPEL&＃39;S TOOL CLEANER 99610 - - 

SURFACE PREPARATION: New steel: Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other  contaminants by high pressure fresh water cleaning. Abrasive blasting to Sa 2½-3 (ISO 8501-1:2007) depending on area of use. Minimum surface profile corresponding to Rugotest No. 3, BN11a, KeaneTator Comparator, 5.5 G/S, or ISO Comparator Coarse (G) - or as per specification for the subsequent  coat(s). After blasting, clean the surface carefully from abrasives and dust. Repair and maintenance: Remove oil and grease etc. thoroughly with suitable detergent. Remove  salts and other contaminants by high pressure fresh water cleaning. On pit-corroded surfaces, excessive amounts of salt residues may call for high pressure water jetting, wet abrasive blasting or, alternatively, dry abrasive blasting, high pressure fresh water hosting, drying, and finally dry abrasive  blasting again. APPLICATION CONDITIONS: Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation. Minimum temperature for application is 5°C/41°F, preferably above 10°C/50°F. Relative humidity  maximum 80 %, preferably below 60%. The temperature of the paint itself should be: Between 15°C (59°F) and 25°C (77°F). In confined spaces provide adequate ventilation during application and drying. PRECEDING COAT: SUBSEQUENT COAT: None. Recommended systems are: HEMPADUR MULTI-STRENGTH 35530, HEMPADUR MULTISTRENGTH 45751. HEMPADUR 15590 can be used as a blast primer. REMARKS: Film thicknesses/thinning: May be specified in another film thickness than indicated depending on purpose and area of use. This  will alter spreading rate and may influence drying time and recoating interval. Normal range dry is: 30-50 micron/1.2-2 mils. Note: HEMPADUR 15590 For professional use only. Overcoating: Overcoating intervals related to later conditions of exposure: If the maximum overcoating interval is  exceeded, roughening of the surface is necessary to ensure intercoat adhesion. Before overcoating after exposure in contaminated environment, clean the surface thoroughly with  high pressure fresh water hosing and allow drying. A specification supersedes any guideline overcoat intervals indicated in the table. X Move PDS Disclaimer to Second page Overcoating note: The coating is to be applied in a dry film thickness as near as possible to the specified: 40 micron. Film formation of each coat has to be of good quality, free from defects such as pinholes and without  any dry spray. Drying and curing conditions have to be according to APPLICATION CONDITIONS until full curing has  been obtained. No kind of surface contamination must exist except loose dust, abrasives, loose dry-spray, which is  possible to remove by vacuum cleaning before overcoating. The surface MUST be completely clean before overcoating. The coating is to be checked carefully and  should have no patchy, whitish, and/or greasy formation, which can hinder adhesion of the subsequent  coat. Exudation of the curing agent causes the mentioned patchy, whitish, and/or greasy formation, which  will take place if the product is applied at low temperatures without proper induction time and/or if the  coating is exposed to water (rain, condensation) during drying and curing. Overcoating intervals: According to specification. The stated minimum overcoating interval may be halved for areas not intended for water immersion. Depending on actual local conditions, extended maximum overcoating interval may apply. Contact  Hempel for more information. If the maximum over coating interval is exceeded, roughening of the  surface is necessary to ensure intercoat adhesion. Before overcoating after exposure in contaminated  environment, clean the surface thoroughly by high pressure water cleaning and allow drying. Theoduct will resist a hosing down of the surface 8 hours after application at a steel temperature of  20°C/68°F. Overcoating intervals: ISSUED BY: HEMPEL A/S 

1.东莞市景鹏船舶机械有限公司是一家专业机械加工、生产、商贸为一体的专业综合型公司。目前公司涂料商贸与**行业50强合作的品牌有：佐敦涂料、海虹老人牌涂料、PPG涂料、式玛涂料、亚美隆涂料、三和涂料。
　　 公司坚持“信守承诺、诚信经营、优质产品、合理价格、科学施工”的经营理念，坚持科学管理及现代化施工设备赢得客户的一致**。我们将一如既往以真诚、优质的服务竭诚为您服务。

   联系人：王小姐
   *    0769-86658302

2.海虹老人牌油漆(中国)有限公司是老人牌集团旗下实力的分支之一，成立于1992年，是老人牌集团与中国香港招商局**有限公司合资组建。
老人牌集团在**拥有28家工厂，110个销售办事处，154个存货点,以高质量的涂料产品**世界各地。海虹老人牌的业务领域包括中国大陆、中国香港及中国澳门地区。公司总部设在中国香港，在中国境内共有三家工厂（蛇口、昆山、烟台）、七个主要办事处（北京、大连、青岛、上海、成都、广州、深圳），广阔的地理覆盖面，使公司具备在一定时间内将产品运送至客户手上。
质量与服务的承诺老人牌集团是世界涂料工业的良好者之一，质量和服务是推动我们前行的动力。我们生产和销售多种高质量的船舶漆、集装箱漆、工业防护漆和装饰道路漆。
 
3.挪威佐敦集团公司是***的三大海洋及工业涂料生产商，总部设在环境优美的挪威山德福佐市，成立于1926年，有**过70年的悠久历史
。在欧洲、中东、亚洲、太平洋和非洲拥有40多家工厂。分支机构较是 遍布世界的各个角落。并在挪威、美国、韩国、马来西亚、迪拜设立
了五个研究开发中心，以此保证佐敦的涂料技术在世界上始终处于良好地位。
   佐敦提供保护建筑 物、工业、船舶、离岸平台的各种涂料产品，
抵抗自然和人类所造成的较坏冲击。佐敦也是世界上少数同时荣获ISO9002质量管理体系认证与 ISO14001环保认证的厂商之一。 

通过不断的研发进步，佐敦船舶油漆一 定会为您的远航提供的支持。为了保证我们的涂料施工后达到较理想的效果，
不论客户需要我们的产品数量多少，我们均委派具有丰富施工经验的技术人员亲临 现场指导施工，以保证工程的质量。
他们的足迹已经遍及世界各地。 作为一家**性跨国公司，我们有着****的生产技术和管理经验，
     我们一直本着兢兢业业、求实创新的原则为客户提供较优良的服务。我们的涂料已经广泛的使 用于外高桥造船基地
，厦门**会展中心、Praxair 气体储罐、振华港机、日照电厂、上海新**博览中心、广州新白云机场、鞍钢新轧-蒂森克虏伯钢结构厂
房、拜尔厂房和船舶制造与维护等各类项目。